根据马氏体不锈钢在连铸浇注过程中的凝固收缩特性,分析连铸浇注过程中易引发表面纵裂的原因,提出应对措施,从而有效地避免板坯表面纵裂的产生。
Based on the slab solidification and shrinkage characteristics of martensitic stainless steel, the causes which induce the surface longitudinal cracking, were analyzed. Countermeasures were put forward and performed to avoid surface longitudinal cracking on slabs effectively.
出处
《连铸》
2007年第6期39-40,共2页
Continuous Casting
关键词
板坯表面
纵裂
马氏体不锈钢
slab surface,longitudinal cracking, martensitie stainless steel