Al2O3 short fiber reinforced La-bearing Al-5%Cu alloy was fabricated by squeeze casting, and the solidified structure and the solute segregation during alloy solidification were studied. The results indicated that La has been enriched near the interface which is favorable to improve the wettability between the fiber and At alloy, but the RE-rich phase was not formed at the interface. At the end of the solidification of the composites, the change of the solute in the surplus liquid phase results in the type of matrix alloy being changed because of the selective crystallization, and the segregation at the interface is finally formed. There is no special influence by La on the Cu segregation in the matrix alloy.
Al2O3 short fiber reinforced La-bearing Al-5%Cu alloy was fabricated by squeeze casting,and the solidified structure and the solute segregation during alloy solidification were studied.The results indicated that La has been enriched near the interface which is favorable to improve the wettability between the fiber and Al alloy,but the RE-rich phase was not formed at the interface.At the end of the solidification of the composites,the change of the solute in the surplus liquid phase results in the type of matrix alloy being changed because of the selective crystallization,and the segregation at the interface is finally formed.There is no special influence by La on the Cu segregation in the matrix alloy.
基金
The study is supported by the Key Research Program of the Ministry of National Education(Authorized No.:00191)
the Natural Science Foundation of Jiangxi Province(Authorized No.:0150032).