摘要
研究了采用内氧化法制备的Al2O3/Cu复合材料在载流条件下的干滑动摩擦磨损性能,结果表明,在相同条件下,Al2O3/Cu复合材料的抗摩擦磨损性能明显优于紫铜;当电流一定时,随着速度与载荷的增加,销试样的磨损率增加,摩擦因数降低。Al2O3/Cu复合材料销试样表层发生了磨粒磨损和粘着磨损,紫铜表层主要发生了粘着磨损。在试验范围内,质量分数为0.60%的Al2O3的Cu基复合材料比质量分数为0.24%的磨损率和摩擦因数低。
The dry wear and friction resistance of Al_2O_3/Cu composites prepared by internal oxidation method have been examined under the condition of loading.The results revealed that the wear and friction resistance of Al_2O_3/Cu composites are superior to that of red copper under the same condition.The weight loss of the samples is increased and friction factor is decreased with increasing in speed and loading at a given current.The abrasive and adhesion wear are observed in surface of Al_2O_3/Cu composites samples,while the adhesion wear in surface of red copper is generated.The weight loss and friction factor of the Al_2O_3/Cu composites with 0.60% Al_2O_3 content is lower than that of ones with 0.24% Al_2O_3 content under the experimental condition.
出处
《特种铸造及有色合金》
CAS
CSCD
北大核心
2007年第12期960-962,共3页
Special Casting & Nonferrous Alloys
基金
河南省高校杰出科研人才创新工程项目(2007KYCX008)
河南省高等学校青年骨干教师资助计划项目
河南省教育厅科技攻关项目(2007430004)
河南科技大学重大科技前期预研专项(2005ZD003)
河南科技大学人才科研基金项目(of023)