摘要
CuO nanoparticle was synthesized via wet chemical method and was characterized diffraction (XRD), nitrogen adsorption-desorption, and scanning electron microscopy (SEM) by X-ray Catalytic oxidation of cumene with molecular oxygen was studied over CuO nanoparticle. The catalysts showed markedly higher activities as compared to CuO prepared by conventional method, CuO/Al2O3, or homogeneous copper catalyst under comparable reaction conditions. The cumene conversion, cumene hydroperoxide (CHP) yield, and selectivity using 0.25 g CuO nanoparticle catalyst and 0.1 mol cumene at 358 K for 7 h were 44.2%, 41.2% and 93.2%, respectively. The catalyst can be recycled. After 6 recycled experiments, no loss of catalytic activity was observed.
CuO nanoparticle was synthesized via wet chemical method and was characterized diffraction (XRD), nitrogen adsorption-desorption, and scanning electron microscopy (SEM) by X-ray Catalytic oxidation of cumene with molecular oxygen was studied over CuO nanoparticle. The catalysts showed markedly higher activities as compared to CuO prepared by conventional method, CuO/Al2O3, or homogeneous copper catalyst under comparable reaction conditions. The cumene conversion, cumene hydroperoxide (CHP) yield, and selectivity using 0.25 g CuO nanoparticle catalyst and 0.1 mol cumene at 358 K for 7 h were 44.2%, 41.2% and 93.2%, respectively. The catalyst can be recycled. After 6 recycled experiments, no loss of catalytic activity was observed.
基金
This work is supported by the Natural Science Foundation of South China University of China(143E5041280)