A doubly resonant ZnGeP2 （ZGP） optical parametric oscillator （OPO） pumped by a novel Tm,Ho：GdVO4 laser was demonstrated. Cryogenic Tin（5 at.-%）, Ho（0.5 at.-%）：GdVO4 laser with high pulse repetition frequency （PRF） of 10 kHz at 2.05 μm was employed as pumping source of ZGP OPO. The 15-mm-long ZGP crystal, 55° cut for I-type phase-matching with low absorption coefficient less than 0.05 cm^-1 at 2 μm, was placed in a piano-piano cavity with resonator length of 30 mm. The ZGP OPO generated a total combined output power of 1.2 W at 3.75 and 4.52 μm under pumping power of 5.3 W, corresponding to slope efficiency of 40% from incident 2μm laser power to midinfrared （Mid-IR） output. A widely tunable range from 3.0 to 6.5 μm was achieved by changing the crystal angle only 3.5°.
A doubly resonant ZnGeP2 （ZGP） optical parametric oscillator （OPO） pumped by a novel Tm,Ho：GdVO4 laser was demonstrated. Cryogenic Tin（5 at.-%）, Ho（0.5 at.-%）：GdVO4 laser with high pulse repetition frequency （PRF） of 10 kHz at 2.05 μm was employed as pumping source of ZGP OPO. The 15-mm-long ZGP crystal, 55° cut for I-type phase-matching with low absorption coefficient less than 0.05 cm^-1 at 2 μm, was placed in a piano-piano cavity with resonator length of 30 mm. The ZGP OPO generated a total combined output power of 1.2 W at 3.75 and 4.52 μm under pumping power of 5.3 W, corresponding to slope efficiency of 40% from incident 2μm laser power to midinfrared （Mid-IR） output. A widely tunable range from 3.0 to 6.5 μm was achieved by changing the crystal angle only 3.5°.
基金
This work was supported by the Program of Excellent Team in Harbin Institute of Technology