采用离线测定的方式对车轮钢精炼-连铸过程氢含量的变化规律进行了现场试验,确定车轮钢增氢的关键环节,为制定车轮钢防增氢措施提供依据。
The field test of hydrogen content change in wheel steel during LF-CC process was done where off-line inspecting method is used. The key hydrogenation stage for wheel steel is determined and provide basis for antihydrogenation measures.