Study on activity evaluation of activated coal-gangue and the hydration process

Chemical compositions,mineral compositions and the activated mechanism of the coal-gangue were analyzed. And pozzolana activities of the coal-gangue were evaluated after activated. Moreover,hydration heat and hydration compositions of activated coal-gangue-calcium oxide system,as well as hydration degree and hardened paste microstructures of activated coal-gangue-cement system were studied. Results show that pozzolana activities of the activated coal-gangue root in amorphous SiO2 and activated Al2O3. With the exciting of gypsum,the reaction of activated coal-gangue and Ca(OH)2 would produce hydration products as ettringite,calcium silicate hydrate,and calcium aluminate. The relationship between the curing age and the content of Ca(OH)2 in coal-gangue-cement system was ascertained. Unhydrated particles in the coal-gangue-cement paste were more than that in the neat cement paste at the same hydration periods,and even existed at the later stage of hydration. Furthermore,the activated coal-gangue could inhibit growth and gathering of the calcium oxide crystal,and improve the structure of hardened cement paste.

Chemical compositions, mineral compositions and the activated mechanism of the coal-gangue were analyzed. And pozzolana activities of the coal-gangue were evaluated after activated. Moreover, hydration heat and hydration compositions of activated coal-gangue-calcium oxide system, as well as hydration degree and hardened paste microstructures of activated coal-gangue-cement system were studied. Results show that pozzolana activities of the activated coal-gangue root in amorphous SiO2 and activated Al2O3. With the exciting of gypsum, the reaction of activated coal-gangue and Ca（OH） 2 would produce hydration products as ettringite, calcium silicate hydrate, and calcium aluminate. The relationship between the curing age and the content of Ca （OH）2 in coal-gangue-cement system was ascertained. Unhydrated particles in the coalogangue-cement paste were more than that in the neat cement paste at the same hydration periods, and even existed at the later stage of hydration. Furthermore, the activated coal-gangue could inhibit growth and gathering of the calcium oxide crystal, and improve the structure of hardened cement paste.