采用以含ITO导电层的柔性透明PET基片作为衬底,荧光材料TBPe、Rubrene分别掺杂在主体材料CBP和Balq中作为蓝色发光层和橙红色发光层,制备了双发光层白色柔性有机电致发光器件(FOLED)。通过适当调节发光层的掺杂比例和厚度,得到了发光性能理想的白光器件。测量表明,制备的器件色稳定性很好,色度随外加驱动电压在很大范围内变化很小,且其色坐标均非常接近于白色等能点。当电流密度为50mA/cm2时,器件最高外量子效率达到0.9%。通过抗弯折性能的测试证明,可以基本实现柔性显示的目的。
We designed a device of new multblayer structure and carried out the experiments on white light-emitting. The structure of the device is PET/ITO/PVK:TPD/CBP:TBPe(20nm)/BAIq:Rubrene (10 nm)/BCP(15 nm)/Alqa (25 nm)/ Mg:Ag(1 000 nm)/Ag(20 nm). The bright and steady light emitting is obtained,and the brightness of the devices comes to 3 500cd/m^2 (at driving voltage of 18 V). The commission international De L' Eclariage(CIE) coordination of the devices is very stable at (0.34, 0.33) while the applied voltage varies from 9 V to 13 V. The maximum quantum is 0.9%. The white- light-emitting characteristics of the devices are explained by the diagram of current density-voltage,optical current-voltage and current density-quantum efficiency, which are measured using Keithley 485 Picoammeter and 2400 SourceMeter. Last, we also discuss the emitting mechanism of the material and the devices.
出处
《光电子.激光》
EI
CAS
CSCD
北大核心
2008年第2期143-145,共3页
Journal of Optoelectronics·Laser
基金
国家自然科学基金资助项目(60576038)
国家自然科学基金委和英国皇家学会联合资助项目
天津市科委重点基金资助项目(06TXTJJC14603)
天津市“材料物理与化学”重点学科资助项目