Different compositions of yttrium silicates coatings were deposited on SiC-C/C by plasma spraying and an outer borosilicate glass was applied on the yttrium silicates coatings surfaces. The structure of the multi-layer coatings was characterized by XRD and SEM analyses. High temperature oxidation behavior of the multi-layer coatings coated C/C composites was investigated. Results show that SiC/2SiO2 Y2O3/1.5SiO2 Y203/ SiO2 Y2O3/glass multi-layer coating has better high temperature oxidation resistance, protecting carbon/ carbon composites from oxidation at 1 773 K in air for 164 h with the weight loss of 1.65%. The oxidation weight loss of the coated C/C with time accorded with parabolic rule in the temperature range 1 573 K-1 873 K; and the corresponding oxidation activation energy of the coated carbon/carbon composites is 132.2 kJ/mol.
Different compositions of yttrium silicates coatings were deposited on SiC-C/C by plasma spraying and an outer borosilicate glass was applied on the yttrium silicates coatings surfaces. The structure of the multi-layer coatings was characterized by XRD and SEM analyses. High temperature oxidation behavior of the multi-layer coatings coated C/C composites was investigated. Results show that SiC/2SiO2 Y2O3/1.5SiO2 Y203/ SiO2 Y2O3/glass multi-layer coating has better high temperature oxidation resistance, protecting carbon/ carbon composites from oxidation at 1 773 K in air for 164 h with the weight loss of 1.65%. The oxidation weight loss of the coated C/C with time accorded with parabolic rule in the temperature range 1 573 K-1 873 K; and the corresponding oxidation activation energy of the coated carbon/carbon composites is 132.2 kJ/mol.
基金
Supported by National Natural Science Foundation of China(No.50772063)
the Program for New Century Excellent Talents in University(No.NCET-06-0893)