Wear-resistant laser-induced thermite reaction Al2O3 ceramic coatings can be fabricated on pure Al and AA7075 aluminum alloy by laser cladding （one-step method） and laser cladding followed by laser re-melting （two-step method） using mixed powders CuO-Al-SiO2 in order to improve the wear properties of aluminum and aluminum alloy, respectively. The microstructure of the coatings was characterized by scanning electron microscopy （SEM） and X-ray diffraction （XRD）. The wear resistance of the coatings was evaluated under dry sliding wear test condition at room temperature. Owing to the presence of hard α-Al2O3 and γ-Al2O3 phases, the coatings exhibited excellent wear resistance. In addition, the wear resistance of the coatings fabricated by two-step method is superior to that of the coatings fabricated by one-step method.
Wear-resistant laser-induced thermite reaction Al2O3 ceramic coatings can be fabricated on pure Al and AA7075 aluminum alloy by laser cladding （one-step method） and laser cladding followed by laser re-melting （two-step method） using mixed powders CuO-Al-SiO2 in order to improve the wear properties of aluminum and aluminum alloy, respectively. The microstructure of the coatings was characterized by scanning electron microscopy （SEM） and X-ray diffraction （XRD）. The wear resistance of the coatings was evaluated under dry sliding wear test condition at room temperature. Owing to the presence of hard α-Al2O3 and γ-Al2O3 phases, the coatings exhibited excellent wear resistance. In addition, the wear resistance of the coatings fabricated by two-step method is superior to that of the coatings fabricated by one-step method.
基金
the Open Fund of the State Key Laboratory of Plastic Forming Simulation and Mould Technology in Huazhong University of Science and Technology(No.05-14)
the Open Fund of the State Key Laboratory of Solidification Processing in Northwestern Polytechnic University(No.05-10)