摘要
To investigate how the popular magnesium alloy AZ31 sheet(aluminum 3%,zinc 1%)behaves in cold working,deep drawing experiments at room temperature,along with finite element(FE)simulation,were performed on the cold forming sheet of the AZ31 alloy after being annealed under various conditions.The activities were focused on the fracture pattern,limit drawing ratio(LDR),deformation load,thickness distribution,anisotropic effect,as well as the influences of the annealing conditions and tool configuration on them.The results display that punch shoulder radius instead of die clearance,has much influence on the thickness distribution.The anisotropy is remarkable in cold working,which adversely impacts the LDR.The fracture often happens on the side wall at an angle to axis of the deformed specimen.The results also imply that the LDR for the material under present experimental conditions is 1.72,and annealing the material at 450 ℃ for 1 h may be preferable for the cold deep drawing.
To investigate how the popular magnesium alloy AZ31 sheet （aluminum 3%, zinc 1%） behaves in cold working, deep drawing experiments at room temperature, along with finite element（FE） simulation, were performed on the cold forming sheet of the AZ31 alloy after being annealed under various conditions. The activities were focused on the fracture pattern, limit drawing ratio（LDR）, deformation load, thickness distribution, anisotropic effect, as well as the influences of the annealing conditions and tool configuration on them. The results display that punch shoulder radius instead of die clearance, has much influence on the thickness distribution. The anisotropy is remarkable in cold working, which adversely impacts the LDR. The fracture often happens on the side wall at an angle to axis of the deformed specimen. The results also imply that the LDR for the material under present experimental conditions is 1.72, and annealing the material at 450 ℃ for 1 h may be preferable for the cold deep drawing.
出处
《中国有色金属学会会刊：英文版》
EI
CSCD
2008年第1期86-91,共6页
Transactions of Nonferrous Metals Society of China
关键词
AZ31镁合金
冷压制
各向异性
有限元素模拟
AZ31 magnesium alloy
cold deep drawing
anisotropy
limit drawing ratio
finite element simulation