Prediction of grain size for large-sized aluminium alloy 7050 forging during hot forming 被引量:10

Prediction of grain size for large-sized aluminium alloy 7050 forging during hot forming
下载PDF
导出
摘要 A numerical approach for process optimization and microstructure evolution of lager-sized forging of aluminium alloy 7050 was proposed, which combined a commercial FEM code Deform 3D with empirical models. To obtain the parameters of empirical constitutive equation and dynamic recrystallization models for aluminium alloy 7050, the isothermal compression tests of 7050 samples were performed on Gleeble-1500 thermo-simulation machine in the temperature range of 250-450 ℃ and strain rate of 0.01-10 s-1, and the metallograph analysis of the samples were carried out on a Leica DMIRM image analyzer. The simulation results show that the dynamic recrystallization in the central area of the billet occurs more easily than that on the edge. Repetitious upsetting and stretching processes make the billet deform adequately. Among several forging processes e.g. upsetting, stretching, rounding and flatting, the stretching process is the most effective way to increase the effective strain and refine the microstructure of the billet. As the forging steps increase, the effective strain rises significantly and the average grain size reduces sharply. Recrystallized volume fractions in most parts of the final forging piece reach 100% and the average grain size reduces to 10 μm from initial value of 90 μm. A numerical approach for process optimization and microstructure evolution of lager-sized forging of aluminium alloy 7050 was proposed, which combined a commercial FEM code Deform 3D with empirical models. To obtain the parameters of empirical constitutive equation and dynamic recrystallization models for aluminium alloy 7050, the isothermal compression tests of 7050 samples were performed on Gleeble-1500 thermo-simulation machine in the temperature range of 250-450℃ and strain rate of 0.01-10 s^-1, and the metallograph analysis of the samples were carried out on a Leica DMIRM image analyzer. The simulation results show that the dynamic recrystallization in the central area of the billet occurs more easily than that on the edge. Repetitious upsetting and stretching processes make the billet deform adequately. Among several forging processes e.g. upsetting, stretching, rounding and flatting, the stretching process is the most effective way to increase the effective strain and refine the microstructure of the billet. As the forging steps increase, the effective strain rises significantly and the average grain size reduces sharply. Recrystallized volume fractions in most parts of the final forging piece reach 100% and the average grain size reduces to 10 μm from initial value of 90 μm.
出处 《Journal of Central South University of Technology》 EI 2008年第1期1-5,共5页 中南工业大学学报(英文版)
基金 Project(2005CB724105) supported by the National Basic Research Program of China Project (IRT0549) supported by the Program for Changjiang Scholars and Innovative Research Team in University
关键词 aluminium alloy 7050 grain size FORGING FEM simulation 铝合金 晶粒尺寸 锻造 有限元法 热成型
  • 相关文献

参考文献12

二级参考文献41

  • 1张辉,彭大暑,杨立斌,孟力平.Recrystallization model for hot-rolling of 5182 aluminum alloy[J].中国有色金属学会会刊:英文版,2001,11(3):382-386. 被引量:3
  • 2ZHANG Hui,PENG Da shu,YANG Li bin,MENG Li ping (Department of Materials Science and Engineering, Central South University, Changsha 410083, China).Flow stress equation for multipass hot-rolling of aluminum alloys[J].Journal of Central South University of Technology,2001,8(1):13-17. 被引量:7
  • 3张坤,刘志义,冯春.添加微量Ag对高Zn超高强铝合金微观组织和力学性能的影响[J].中国有色金属学报,2005,15(1):116-122. 被引量:16
  • 4ZHOU M, CLODE M P. Constitutive Equations for Modeling Flow Softening Due to Dynamic Recovery and Heat Generation During Plastic Deformation [J]. Mechanics of Materials, 1998,27(2): 63-76.
  • 5CHO S H, KIM S I, YOO Y C. Determination of No-recrystallization Temperature of Invar Alloy by Fractional Softening Measurement During the Multistage Deformation [J]. Journal of Materials Science Letters, 1997,16(22): 1836-1837.
  • 6SONNINO C, FORD T, VANARK V. Potentiometric and Potentiostatic Determination of the Corrosion Rate of Welded 2519 Aluminum Alloy [J]. ASTM Special Technical Publication, 1991, (1134): 132-140.
  • 7DEVICENT S M, DEVLETIAN J H, GEDON S A. Weld Properties of the Newly Developed 2519-T87 Aluminum Armor Alloy [J]. Welding Journal, 1988,67(7): 33- 43.
  • 8DYMEK S, DOLLAR M. TEM Investigation of Age-hardenable Al 2519 Alloy Subjected to Stress Corrosion Cracking Tests[J]. Materials Chemistry and Physics, 2003,82(1):1-3.
  • 9CHIA E H, MCQUEEN H J. Microstructure Control in Aluminum Alloy: Deformation, Recovery and Recrystallization[M].NewYork:TMS, 1985.
  • 10KWON O, DEARDO A J. On the Recovery and Recrystallization Which Attend Static Softening in Hot-deformed Copper and Aluminum[J]. Acta Metallurgical, 1990,38(1): 41-54.

共引文献26

同被引文献76

引证文献10

二级引证文献61

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部