摘要
The effect of niobium on glass-formation ability and soft magnetic properties were studied in Fe-Gd-B glassy alloys. The glassy alloys exhibited high glass-formation ability when the element of Nb was added. Bulk glassy rod （Fe0.87Co0.13）68.5Gd3.5Nb3B25 with a diameter up to 3 mm was produced by copper mold casting. The size of the atom might play an important role in increasing glass-formation ability. The coercive force of glassy （Fe0.87Co0.13）71.5.xGd3.sNbxB25 （x=1.2, 1.5, 2, 2.5, 3, 4） alloys decreased after the addition of niobium element and was in the range of 1.5-2.9 A/m. The permeability spectrum of （Fe0.87Co0.13）70.3Gd3.5Nb1.5B25 glassy ribbon showed that the relaxation frequency （f0） was 6.1 MHz.
The effect of niobium on glass-formation ability and soft magnetic properties were studied in Fe-Gd-B glassy alloys. The glassy alloys exhibited high glass-formation ability when the element of Nb was added. Bulk glassy rod （Fe0.87Co0.13）68.5Gd3.5Nb3B25 with a diameter up to 3 mm was produced by copper mold casting. The size of the atom might play an important role in increasing glass-formation ability. The coercive force of glassy （Fe0.87Co0.13）71.5.xGd3.sNbxB25 （x=1.2, 1.5, 2, 2.5, 3, 4） alloys decreased after the addition of niobium element and was in the range of 1.5-2.9 A/m. The permeability spectrum of （Fe0.87Co0.13）70.3Gd3.5Nb1.5B25 glassy ribbon showed that the relaxation frequency （f0） was 6.1 MHz.
基金
Project supported by the National Natural Science Foundation of China (50471094)