To improve the cyclic stability of La-Mg-Ni system alloy, as-cast La0.75Mg0.25Ni3.5Co0.2 alloy was annealed at 1123, 1223, and 1323 K for 10 h in 0.3 MPa argon. The microstructure and electrochemical performance of different annealed alloys were investigated systematically by X-Ray Diffraction （XRD）, Scanning Electron Microscopy （SEM）, X-Ray Photoelectron Spectroscopy （XPS）, and electrochemical experiments. The results obtained by XRD and SEM showed that the as-cast and annealed （1123 K） alloys had multiphase structure containing LaNis, （La, Mg）2（Ni, Co）7 and few LaNi2 phases. When annealing temperatures approached 1223 and 1323 K, LaNi2 phase disappeared. The annealed alloys at 1223 and 1323 K were composed of LaNi5, （La, Mg）2（Ni, Co）7 and （La, Mg）（Ni, Co）3 phases. With increasing annealing temperature, the maximum discharge capacity of the alloy decreased monotonously, but the cyclic stability was improved owing to structure homogeneity and grain growth after annealing, as well as the enhancement of anti-oxidation/corrosion ability and the suppression of pulverization during cycling in KOH electrolyte.
To improve the cyclic stability of La-Mg-Ni system alloy, as-cast La0.75Mg0.25Ni3.5Co0.2 alloy was annealed at 1123, 1223, and 1323 K for 10 h in 0.3 MPa argon. The microstructure and electrochemical performance of different annealed alloys were investigated systematically by X-Ray Diffraction （XRD）, Scanning Electron Microscopy （SEM）, X-Ray Photoelectron Spectroscopy （XPS）, and electrochemical experiments. The results obtained by XRD and SEM showed that the as-cast and annealed （1123 K） alloys had multiphase structure containing LaNis, （La, Mg）2（Ni, Co）7 and few LaNi2 phases. When annealing temperatures approached 1223 and 1323 K, LaNi2 phase disappeared. The annealed alloys at 1223 and 1323 K were composed of LaNi5, （La, Mg）2（Ni, Co）7 and （La, Mg）（Ni, Co）3 phases. With increasing annealing temperature, the maximum discharge capacity of the alloy decreased monotonously, but the cyclic stability was improved owing to structure homogeneity and grain growth after annealing, as well as the enhancement of anti-oxidation/corrosion ability and the suppression of pulverization during cycling in KOH electrolyte.
基金
Project supported by the National Natural Science Foundation of China(50642033
50701011)
Key Technologies R&D Program of Inner Mongolia, China (20050205)
Natural Science Foundation of Inner Mongolia, China (200711020703)