We report the adsorption of phosphate and discuss the mechanisms of phosphate removal from aqueous solution by burst furnace slag (BFS) and steel furnace slag (SFS). The results show that the adsorption of phosphate on the slag was rapid and the majority of adsorption was completed in 5~10 min. The adsorption capacity of phosphate by the slag was reduced dramatically by acid treatment. The relative contribution of adsorption to the total removal of phosphate was 26%~28%. Phosphate adsorption on BFS and SFS follows the Freundlich isotherm, with the related constants of k 6.372 and 1/n 1.739 for BFS, and of k 1.705 and 1/n 1.718 for SFS. The pH and Ca2+ concentration were decreased with the addition of phosphate, suggesting the formation of calcium phosphate precipitation. At pH 2.93 and 6.93, phosphate was desorbed by about 36%~43% and 9%~11%, respectively. These results indicate that the P adsorption on the slag is not completely reversible and that the bond between the slag particles and adsorbed phosphate is strong. The X-ray diffraction (XRD) patterns of BFS and SFS before and after phosphate adsorption verify the formation of phosphate salts (CaHPO4·2H2O) after adsorption process. We conclude that the removal of phosphate by BFS and SFS is related to the formation of phosphate calcium precipitation and the adsorption on hydroxylated oxides. The results show that BFS and SFS removed phosphate nearly 100%, indicating they are promising adsorbents for the phosphate removal in wastewater treatment and pollution control.
We report the adsorption of phosphate and discuss the mechanisms of phosphate removal from aqueous solution by burst furnace slag （BFS） and steel furnace slag （SFS）. The results show that the adsorption of phosphate on the slag was rapid and the majority of adsorption was completed in 5-10 min. The adsorption capacity of phosphate by the slag was reduced dramatically by acid treatment. The relative contribution of adsorption to the total removal of phosphate was 26%-28%. Phosphate adsorption on BFS and SFS follows the Freundlich isotherm, with the related constants of k 6.372 and 1/n 1.739 for BFS, and of k 1.705 and 1/n 1.718 for SFS. The pH and Ca^2＋ concentration were decreased with the addition of phosphate, suggesting the formation of calcium phosphate precipitation. At pH 2.93 and 6.93, phosphate was desorbed by about 36%-43% and 9%-11%, respectively. These results indicate that the P adsorption on the slag is not completely reversible and that the bond between the slag particles and adsorbed phosphate is strong. The X-ray diffraction （XRD） patterns of BFS and SFS before and after phosphate adsorption verify the formation of phosphate salts （CaHPO4·2H2O） after adsorption process. We conclude that the removal of phosphate by BFS and SFS is related to the formation of phosphate calcium precipitation and the adsorption on hydroxylated oxides. The results show that BFS and SFS removed phosphate nearly 100%, indicating they are promising adsorbents for the phosphate removal in wastewater treatment and pollution control.
基金
Project supported by the Foundation for the Author of NationalExcellent Doctoral Dissertation of China (No. 200149)
the NaturalScience Foundation of Zhejiang Province (No. R305078), China
关键词
废物处理
综合利用
送风炉
炉渣
Phosphate removal, Blast furnace slag （BFS）, Steel furnace slag （SFS）, Adsorption, Precipitation