摘要
The silica coated aluminum composite particles were prepared by hydrolysis–condensation polymerization of tetraethylorthosilicate(TEOS)on the surface of aluminum particle.The structure,morphology,and properties of the silica coated aluminum were studied.The peaks of Si—O—Si are presented in the Fourier transform infrared(FT-IR)spectrum of the composite particles.The thickness of the silica shell is about 80 nm according to the results of transmission electron microscopy(TEM)and laser particle size analysis,while the mean diameter of the aluminum particle is 7.13μm.The mass fraction of silica in the sample was determined by fluorescent X-ray spectrometry(XRF).Result of the thermogravimetric analysis(TGA)indicates that thermal stability of silica coated aluminum particles is better than that of pure aluminum particles at low temperature while more reactive at high temperature.
The silica coated aluminum composite particles were prepared by hydrolysis-condensation polymerization of tetraethylorthosilicate（TEOS） on the surface of aluminum particle. The structure, morphology, and properties of the silica coated aluminum were studied. The peaks of Si-O-Si are presented in the Fourier transform infrared （FT-IR） spectrum of the composite particles. The thickness of the silica shell is about 80 nm according to the results of transmission electron microscopy（TEM） and laser particle size analysis, while the mean diameter of the aluminum particle is 7.13 μm. The mass fraction of silica in the sample was determined by fluorescent X-ray spectrometry（XRF）. Result of the thermogravimetric analysis（TGA） indicates that thermal stability of silica coated aluminum particles is better than that of pure aluminum particles at low temperature while more reactive at high temperature.
出处
《中国有色金属学会会刊：英文版》
EI
CSCD
2008年第2期378-382,共5页
Transactions of Nonferrous Metals Society of China
基金
Project(50306008)supported by the National Natural Science Foundation of China
关键词
铝
微粒
硅土
分析方法
silica
aluminum particle
coating
core-shell
oxidation