摘要
A wolfram tailing glass contains a substantial proportion of wolfram tailing and other ingredients such as fcldspar, limestone, soda,thenardite and fluorbaryt. Samples of wolfram glasses were implanted with tantalum ions at doses of 5×1016. 1×1017 and 2 ×1017 ions/cm2at room temperature, then were treated at 700℃ for 1h and 900℃ for 2h. Scanning electron microscope and X-ray diffraction analysis were applied to study the morphology and crystal phases of unimplanted and implanted heat-treatment samples.The results show that there is no change of crystal phases in the unimplanted and implanted heated samples but the crystal valumes of wollastonite of implanted is more than that of unimplanted sample. It can be seen that the crystals become fine and dense after implantation, because the concentration of nucleation sites may increase with increasing tantalumions dose.
A wolfram tailing glass contains a substantial proportion of wolfram tailing and other ingredients such as fcldspar, limestone, soda,thenardite and fluorbaryt. Samples of wolfram glasses were implanted with tantalum ions at doses of 5×1016. 1×1017 and 2 ×1017 ions/cm2at room temperature, then were treated at 700℃ for 1h and 900℃ for 2h. Scanning electron microscope and X-ray diffraction analysis were applied to study the morphology and crystal phases of unimplanted and implanted heat-treatment samples.The results show that there is no change of crystal phases in the unimplanted and implanted heated samples but the crystal valumes of wollastonite of implanted is more than that of unimplanted sample. It can be seen that the crystals become fine and dense after implantation, because the concentration of nucleation sites may increase with increasing tantalumions dose.
出处
《玻璃与搪瓷》
CAS
北大核心
1997年第3期36-39,共4页
Glass & Enamel
基金
大连理工大学三束材料改性国家重点联合实验室资助
关键词
微晶玻璃
晶化
钽
离子注入
钨渣
Tantalum ion-implantation Crystallization Wolfram tailing glass-ceramic