摘要
采用"超声波、助剂-溶液-水悬浮-蒸馏-成型"和超临界流体反溶剂(SAS)包覆技术研究了亚微米奥克托今(HMX)/氟橡胶(FPM2602)混合炸药造型粉的制造工艺,并用组分分析、扫描电镜(SEM)和傅立叶变换红外光谱(FT-IR)等方法进行了表征,对两种制备工艺得到的混合炸药的起爆性能进行了测试。结果表明,超声波、助剂-溶液-水悬浮-蒸馏-成型由于自身的一些缺点不适合制备超细混合炸药;而SAS包覆技术适合制备超细混合炸药,是一种绿色环保技术。
The submicron HMX/ FPM2602 composite explosive was prepared by solution-aqueous suspension technology with ultrasound and supercritical fluids antisolvent (SAS) coating technology, and were analyzed by component analysis, scanning electron microscope (SEM) and Fourier transformation infrared spectrometer (FT-IR). Its detonation performance was tested as well. Results indicate that the solution-aqueous suspension technology is not suitable for preparation ultra-fine composite explosive, whereas SAS technology has not any pollution.
出处
《含能材料》
EI
CAS
CSCD
2008年第2期142-145,148,共5页
Chinese Journal of Energetic Materials