High strength Al-Zn-Mg-Cu alloys were prepared by spray deposition and casting techniques. The microstructures of the Al-Zn-Mg-Cu alloys were studied using scanning electron microscopy, transmission electron microscopy, and X-ray diffraction. Secondary phases in the microstructures of the alloys prepared by spray deposition and conventional cast were examined. The results indicate that under the conventional casting condition, the microstructure of the alloy revealed the presence of coarse Al/Mg（ZnCu）2 eutectic phases, and the spray deposited process causes an obvious modification in size, morphology, and distribution of secondary phases in the microstructure as well as reduction of segregation. The superior microstructure of the spray-deposited Al-Zn-Mg-Cu alloy was attributed to the high cooling rate, and associated with the rapid solidification process.
High strength Al-Zn-Mg-Cu alloys were prepared by spray deposition and casting techniques. The microstructures of the Al-Zn-Mg-Cu alloys were studied using scanning electron microscopy, transmission electron microscopy, and X-ray diffraction. Secondary phases in the microstructures of the alloys prepared by spray deposition and conventional cast were examined. The results indicate that under the conventional casting condition, the microstructure of the alloy revealed the presence of coarse Al/Mg（ZnCu）2 eutectic phases, and the spray deposited process causes an obvious modification in size, morphology, and distribution of secondary phases in the microstructure as well as reduction of segregation. The superior microstructure of the spray-deposited Al-Zn-Mg-Cu alloy was attributed to the high cooling rate, and associated with the rapid solidification process.
基金
This work was financially supported by the Major State Basic Besearch Development Program of China (No.2005CB623704)
The authors wish to thank professors Shao B.L.and Liu A.S.(National Analysis and Testing Center for Nonferrous Metals & Electronic Materials,General Research Institute for Nonferrous Metals) for the TEM work,and Li Y.L.(Analysis and Test Center,Beijing Normal University) for SEM work.