摘要
The crystal structure of a sodium titanium oxide Na2TiO3 obtained by high temperature solid state reaction method was determined from single-crystal X-ray diffraction study. The compound crystallizes in the monoclinic system, space group C2/c, Mr = 141.88, a = 9.885（1）, b = 6.4133（8）, c = 5.5048（7） A, β = 115.50（3）°, V = 314.99（7） A^3, Z = 4, Dc = 2.992 g/cm^3, 2 = 0.71073A,μ = 27.80 cm^-1, F（000） = 272, T= 295 K, R = 0.0189 and wR = 0.0512 for 30 variables and 370 contributing unique reflections. The three-dimensional structure in Na2TiO3 is constructed by the TiO（1）4O（2） and NAO（1）3O（2）2 groups. The titanium atoms are grouped in the form of trigonal bipyramid and arranged along the c axis by sharing the edges. The structure is compared with other structures of related A2BO3 compounds.
The crystal structure of a sodium titanium oxide Na2TiO3 obtained by high temperature solid state reaction method was determined from single-crystal X-ray diffraction study. The compound crystallizes in the monoclinic system, space group C2/c, Mr = 141.88, a = 9.885（1）, b = 6.4133（8）, c = 5.5048（7） A, β = 115.50（3）°, V = 314.99（7） A^3, Z = 4, Dc = 2.992 g/cm^3, 2 = 0.71073A,μ = 27.80 cm^-1, F（000） = 272, T= 295 K, R = 0.0189 and wR = 0.0512 for 30 variables and 370 contributing unique reflections. The three-dimensional structure in Na2TiO3 is constructed by the TiO（1）4O（2） and NAO（1）3O（2）2 groups. The titanium atoms are grouped in the form of trigonal bipyramid and arranged along the c axis by sharing the edges. The structure is compared with other structures of related A2BO3 compounds.