Microstructure and mechanical properties of Mg-15wt.%Gd-5 wt.%Y-0.5wt.% Zr alloy were investigated in a series of conditions. The eutectic was dissolved into the matrix and there was no evident grain growth after solntionized at 525 ℃ for 12 h. The evolution of the phase constituents from as-cast to cast-T4 was as follows： α-Mg solid solution＋Mg5（Gd,Y） entectic compound→α-Mg solid solution＋ spheroidized Mg5（Gd, Y） phase→α-Mg supersaturated solid solution＋cuboid-shaped compound （Mg2Y3Gd2）. And the precipitation sequences of Mg-15Gd-5Y-0.5Zr alloy were observed, according to the hardness response to isothermal ageing at 225-300 ℃ for 0-128 h.
Microstructure and mechanical properties of Mg-15wt.%Gd-5 wt.%Y-0.5wt.% Zr alloy were investigated in a series of conditions. The eutectic was dissolved into the matrix and there was no evident grain growth after solntionized at 525 ℃ for 12 h. The evolution of the phase constituents from as-cast to cast-T4 was as follows： α-Mg solid solution＋Mg5（Gd,Y） entectic compound→α-Mg solid solution＋ spheroidized Mg5（Gd, Y） phase→α-Mg supersaturated solid solution＋cuboid-shaped compound （Mg2Y3Gd2）. And the precipitation sequences of Mg-15Gd-5Y-0.5Zr alloy were observed, according to the hardness response to isothermal ageing at 225-300 ℃ for 0-128 h.
基金
the Major State Basic Research Development Program of China (973 Program, 5133001E)