摘要
分析了板坯三角区裂纹的形成机理和形成原因,结合板坯生产情况,查出了主要影响因素,制定并实施了针对性措施,取得了较好的效果。
The essay introduces the formation mechanism of slab crack at triangle area and analyses the foming causes. Main affecting factors are found out according to the slab pro-duction situation at the plant.Counter measures are formulated and executed with good results.
出处
《天津冶金》
CAS
2008年第2期24-25,52,共3页
Tianjin Metallurgy
关键词
板坯
三角区裂纹
原因
分析
控制
措施
slab,crack,triangle area,cause,analysis,control, measures