摘要
The purpose of this paper was to investigate the effects of solution treatment time and Sr-modification on the microstructure and property of the Al-Si piston alloy.It was found that as-cast microstructures of unmodified and Sr-modified Al-Si alloys consisted of a coarse acicular plate of eutectic Si,Cu_3NiAl_6 and Mg_2Si phases in theα-Al matrix but different in size and morphology.Both size and inter-particle spacing of Si particles were significantly changed by increasing the solution treatment time.After a short solution treatment,the coarse acicular plate of the eutectic Si appears to be fragmented.Fully modified microstructure of Sr-modified alloy can reduce the solution treatment time compared to unmodified alloy.The maximum of a peak hardness value is found in the very short solution treatment of both Al-Si piston alloys.Compared to 10 h solution treatment,the solution treatment of 2-4 h is sufficient to achieve appropriate microstructures and hardness. The short solution treatment is very useful to increase the productivity and to reduce the manufacturing cost of the Al-Si piston alloys.
The purpose of this paper was to investigate the effects of solution treatment time and Sr-modification on the microstructure and property of the Al-Si piston alloy.It was found that as-cast microstructures of unmodified and Sr-modified Al-Si alloys consisted of a coarse acicular plate of eutectic Si,Cu_3NiAl_6 and Mg_2Si phases in theα-Al matrix but different in size and morphology.Both size and inter-particle spacing of Si particles were significantly changed by increasing the solution treatment time.After a short solution treatment,the coarse acicular plate of the eutectic Si appears to be fragmented.Fully modified microstructure of Sr-modified alloy can reduce the solution treatment time compared to unmodified alloy.The maximum of a peak hardness value is found in the very short solution treatment of both Al-Si piston alloys.Compared to 10 h solution treatment,the solution treatment of 2-4 h is sufficient to achieve appropriate microstructures and hardness. The short solution treatment is very useful to increase the productivity and to reduce the manufacturing cost of the Al-Si piston alloys.