We reported effect of various alkaline oxides on the broadband infrared luminescence from bismuth-doped aluminophosphate glasses. The samples of （99-x）P2O3-17Al2O3-xR2O-IBi2O3 （R=Li, Na and K, x=0 and 10 in mol%） were prepared under reducing condition controlled by additional carbon powders. The fluorescent intensity decreased with increasing content of alkaline oxides and basicity of host glasses. The 1/e fluorescence lifetime of the 72P2O3-17Al2O3-10R2O-1Bi2O3 （R=Li, Na and K） glasses decreased from 461 to 316 μs, as alkaline ions changed from Li^＋ to K^＋.
We reported effect of various alkaline oxides on the broadband infrared luminescence from bismuth-doped aluminophosphate glasses. The samples of （99-x）P2O3-17Al2O3-xR2O-IBi2O3 （R=Li, Na and K, x=0 and 10 in mol%） were prepared under reducing condition controlled by additional carbon powders. The fluorescent intensity decreased with increasing content of alkaline oxides and basicity of host glasses. The 1/e fluorescence lifetime of the 72P2O3-17Al2O3-10R2O-1Bi2O3 （R=Li, Na and K） glasses decreased from 461 to 316 μs, as alkaline ions changed from Li^＋ to K^＋.
基金
Funded by the National Natural Science Foundation of China (No.50672087 and No.60778039)
National Basic Research Program of China (No.2006CB806000b)
National High Technology Program of China (No.2006AA03Z304)