摘要
yb^3＋-Er^3＋ co-doped Na20-Al2O3-SiO2-P2O5 glasses with different SiO2 content have been fabricated and characterized. Absorption and emission spectra were measured. Judd-Ofelt theory and McCumber theory are performed to analyze the measured absorption spectra. The Judd-Ofelt intensity parameters Ω4 and Ω6 decrease with increasing SiO2 content. The emission cross-section of Er^3＋ decreases from 0.82×10^-20cm^2 to 0.76 × 10^-20cm^2 as the SiO2 content varies from 0 to 20 mol%.
yb^3＋-Er^3＋ co-doped Na20-Al2O3-SiO2-P2O5 glasses with different SiO2 content have been fabricated and characterized. Absorption and emission spectra were measured. Judd-Ofelt theory and McCumber theory are performed to analyze the measured absorption spectra. The Judd-Ofelt intensity parameters Ω4 and Ω6 decrease with increasing SiO2 content. The emission cross-section of Er^3＋ decreases from 0.82×10^-20cm^2 to 0.76 × 10^-20cm^2 as the SiO2 content varies from 0 to 20 mol%.
基金
Funded by the International Cooperation Project of Shanghai Municipal Science and Technology Commission (No.05S207103)