摘要
研究了乳液法PVC(简称乳PVC)、悬浮法PVC(简称悬PVC)和粘合剂用量、阻燃增塑剂、带芯含棉量等因素对橡塑整芯难燃输送带粘合性能的影响。结果表明,在覆盖胶中可用20~25份乳PVC等量替代CR/NBR/氯化聚乙烯(CPE)(40/40/20)配方体系中的NBR,也可用40~60份悬PVC等量替代NBR配方体系中的NBR;浸渍液中增塑剂选择ZRS50/DOP/42%氯化石蜡并用最适宜;覆盖胶中加入粘合剂A,可提高粘合强度,用量宜为15~25份;带芯含棉量为30%~40%较为合理。
The influence of the level of emulsion PVC,suspension PVC and adhesive,the type of flame retardant plasticizer and the cotton content in carcass on the adhesion strength of flame retardant rubber/plastics solid woven conveyor belt was investigated.The results showed that 20~25 phr of emulsion PVC could replace the equivelent proportion of NBR in CR/NBR/CPE(40/40/20) blend and 40~60 phr of suspension PVC cound replace the equivelent proportion of NBR in NBR based compound for belt cover;it was the most suitable to use ZRS 50/DOP/42% chlorinated paraffin as the plasticizer in the dipping solution;the adhesion strength increased with the addition of 1 5~2 5 phr of adhesive A to cover compound;and it was reasonable to use the carcass with 30%~40% cotton content.
出处
《橡胶工业》
CAS
北大核心
1997年第12期715-718,共4页
China Rubber Industry