摘要
用湿化学方法合成了Ce3+/Dy3+及Ce3+/Tb3+共掺GdAl3(BO3)4发光材料。利用X射线衍射仪对其进行了物相分析,结果表明:合成物为纯的六方相GdAl3(BO3)4微晶。利用荧光分光光谱仪进行光谱分析,测定了合成样品的激发和发射光谱。发现在紫外激发下,GdAl3(BO3)4:Dy荧光粉发射出很强的偏黄的白光,其发射峰分别位于480,575和665nm,对应于Dy3+的4F9/2→6H15/2,13/2,11/2跃迁。掺Ce3+对Dy3+起到敏化作用,GdAl3(BO3)4:Dy,Ce发出很亮的暖白光,且强度是GdAl3(BO3)4:Dy的3倍左右。同时,在Ce3+/Tb3+共掺的样品中,由于Ce3+与Tb3+间的能量传递,Tb3+的541nm特征峰显著增强。
Ce3+/Dy3+ and/or Ce3+/Tb3+ codoped GdAl3(BO3)4 phosphors were synthesised by a wet-chemical method. The phosphors were characterized by X-ray diffraction and fluorescence measurements. The GdAl3(BO3)4:Dy phosphors show intense emissions centred at 480, 575, and 665 nm upon excitation by ultraviolet-blue light, which are associated with the typical transitions of 4F9/2→ 6H15/2, 4F9/2→6H13/2, and 4F9/2→ 6H11/2 of Dy3+, respectively. The presence of Ce3+ resulted in an enhancement of Dy3+ emission intensity by a factor of -3. The characteristic green emission at 541 nm of Tb3+ doped GdAl3(BO3)4 has been significantly enhanced with Ce3+ doping, confirming that energy transfer from Ce3+ to Tb3+ happens in the compounds.
出处
《稀有金属材料与工程》
SCIE
EI
CAS
CSCD
北大核心
2008年第A02期568-571,共4页
Rare Metal Materials and Engineering
基金
NSFC(Grant No.50472053)
NCET(Grant No.04-0823)