制备了可用于蓝色TFEL的粉末发光材料MGa2S4:Ce(M=Ca,Sr)并对其晶体结构进行了X射线分析,测量并研究了其激发光谱和发射光谱,研究了Ce3+浓度的变化对CaGa2S4:Ce和SrGa2S4:Ce的激发光谱.发射光谱、色纯度及发光强度的影响,同时研究了基质组份的改变对发光特性的影响.结果表明,CaGa2S4:Ce和SrGa2S4:Ce可发射纯蓝色光,色纯度好.对CaGa2S4:Ce来说,实现其高效率的、纯蓝色发射的最佳Ce3+浓度为6mol%,而SrGa2S4:Ce的最佳Ce3+浓度为3~4mol%.
The blue-emitting phosphor MGa2S4:Ce(M=Ca, Sr) was prepared, and its crystallinity wasanalysed by X-ray diffraction. The excitation and emission spectra of MGa2S4:Ce were measuredand investigated, and the effects of the cerium concentration and the composition of host materialon the PL properties for MGa2S4:Ce powder were studied. The results of PL measurement showedthat MGa2S4:Ce phosphor achieved an even more saturated blue emission, and the optimumcerium concentration for high efficiency and more saturated blue emission was about 6mol% forMGa2S4:Ce, 3.0~4.0mol% for SrGa2S4:Ce.