摘要
以ＰＥＴ、ＥＧ为主要原料，同时加入共聚组分，采用直接酯化－－缩聚法合成共聚酯，对热收缩ＰＥＴ的收经、双折射率、取向度等性能进行了测试。
同被引文献17
-
1尤红星.热收缩性聚酯薄膜的研制[J].塑料加工与应用,1994(2):11-15. 被引量：2
-
2D. M Shelby, M. C Tanner, D. K Horton. Polyester blends and heat shrinkable films made thereform. USA. US 6 599 994. 2003- 07 - 29.
-
3J. B Sublett. Shrinkable copolyester film. USA. US 5 340 624.1994 - 08 - 23
-
4K. W Shih. Plasticized polyester shrink film application. USA. US 5 824 398. 1998 -10 -20
-
5H. Ito, N. Tabota,T. Oko. Heat shrinkable polyester film. USA.US 6 451 445. 2002 -09 - 17
-
6N. Tabota, M. Hashimoto, S. Takabayashi,et al. USA. US 6 447 925. 2002 -09 - 10
-
7Y. Fukuda; S. Utsumi. Shrinkable polyester film. USA. US 4 985 538. 1991 -01 - 15
-
8Y. Fukuda,S. Utsumi,S. Suzuki. Shrinkable copolyester film.USA. US 5 070 180. 1991 - 12 -03
-
9K. W Shih. Clarity and adjustable shrinkage of shrink films using miscible polyester blends. USA. US 5 859 116. 1999 -01 - 12
-
10D. M Shelby,K. W Shih,P. R Little Jr.,et al. Reactor grade copolyesters for shrink film applications. USA. US 6 362 306.2002-04 -26
-
1刘志柱.边界元子域缩聚法分析异质材料界面问题[J].河南机电高等专科学校学报,1999,7(3):31-35.
-
2赵廷凯,张红燕,朱若星,王军高,折胜飞,赵星,李铁虎.碳纳米管/中间相炭微球复合材料锂离子电池负极材料研究[J].功能材料,2014,45(19):19080-19083. 被引量：5
-
3李明德,李耘.鉴别晶相相变类型的一种新方法——双折射率法[J].硅酸盐学报,1997,25(4):485-488.
-
4陈新兵,安忠维.电视用液晶材料的研究进展[J].化学进展,2006,18(2):246-251. 被引量：3
-
5杨妹清.双折射空间分布测定法[J].光机电信息,1998,15(11):17-21.
-
6硼镀酸盐非线性昌体材料研究取得新发现[J].现代材料动态,2010(9):24-24.
-
7张德文.二级近似坐标缩聚法[J].机械强度,1995,17(1):64-66. 被引量：3
-
8陆树苹,程龙,赵萌,李慧.硝化聚三氟苯乙烯的制备及其光学性能[J].功能高分子学报,2015,28(2):130-135. 被引量：2
-
9施立新,吴文士.POM和PONA的量化计算比较[J].通化师范学院学报,2006,27(4):50-52.
-
10张武,王燕.光学非均匀单向纤维复合材料的应力光学行为[J].物理学报,1994,43(7):1192-1202.