The doping effects of La^3＋, Gd^3＋ and Lu^3＋ on the crystal structure and luminescence properties of （Yo96-x LnxCe0.04）3Al5O12（Ln = Gd, La, Lu） phosphors were studied. The X-ray diffraction patterns presented that with the inerease of the doping concentrations of La^3＋ and Gd^3＋ ions, the d-value of （Y0.96-xLnxCe0.04）3Al5O12 （Ln = Gd, La） inereased and the larger the doping ion, the stronger the effect would be. The doping amount causing phase transition in （Y0.96-xLnxCe0.04）3Al5O12 decreased with the inerease of the ionic radii of the doping lanthanide ions （La^3＋： 0.106 nm, Gd^3＋： 0. 094 nm, Lu^3＋ ： 0.083 nm）. The bigger doping ion of Gd^3＋ made the emission of （Y0.96-xGdxCe0.04）3Al5O12 move to red spectral region, but the smaller one of Lu^3＋ made it blue.
The doping effects of La^3＋, Gd^3＋ and Lu^3＋ on the crystal structure and luminescence properties of （Yo96-x LnxCe0.04）3Al5O12（Ln = Gd, La, Lu） phosphors were studied. The X-ray diffraction patterns presented that with the inerease of the doping concentrations of La^3＋ and Gd^3＋ ions, the d-value of （Y0.96-xLnxCe0.04）3Al5O12 （Ln = Gd, La） inereased and the larger the doping ion, the stronger the effect would be. The doping amount causing phase transition in （Y0.96-xLnxCe0.04）3Al5O12 decreased with the inerease of the ionic radii of the doping lanthanide ions （La^3＋： 0.106 nm, Gd^3＋： 0. 094 nm, Lu^3＋ ： 0.083 nm）. The bigger doping ion of Gd^3＋ made the emission of （Y0.96-xGdxCe0.04）3Al5O12 move to red spectral region, but the smaller one of Lu^3＋ made it blue.
基金
Project supported by the National Natural Science Foundation of China (20071031)