The structure evolution of the ZL109 alloy in the process of semi-solid squeeze casting and the mechanical properties of the components were investigated. The results show that （1） the eutectic silicon phase in original billets is refined in the low super-heat casting process; （2） the eutectic structure in billets starts to fuse and the crystals of the eutectic silicon phase are refined further and sphericized in the remelting process of billets; （3） in the semi-solid squeeze casting process, the sphericity of the a phase and the refining of the silicon phase occur, owing to the friction between solid and liquid; （4） in the process of heat treatment, the eutectic a phase aggregates with the primary a phase and the eutectic silicon pieces aggregate together. The elongation of the semi-solid component after heat treatment rises to 1.42%.
The structure evolution of the ZL109 alloy in the process of semi-solid squeeze casting and the mechanical properties of the components were investigated. The results show that （1） the eutectic silicon phase in original billets is refined in the low super-heat casting process; （2） the eutectic structure in billets starts to fuse and the crystals of the eutectic silicon phase are refined further and sphericized in the remelting process of billets; （3） in the semi-solid squeeze casting process, the sphericity of the a phase and the refining of the silicon phase occur, owing to the friction between solid and liquid; （4） in the process of heat treatment, the eutectic a phase aggregates with the primary a phase and the eutectic silicon pieces aggregate together. The elongation of the semi-solid component after heat treatment rises to 1.42%.
出处
《Rare Metals》
SCIE
EI
CAS
CSCD
2008年第3期329-333,F0003,共6页
稀有金属（英文版）