实验研究表明混凝土结构的裂缝并不完全是通常认为的引起钢筋腐蚀，降低结构的耐久性．文章分析了钢筋的腐蚀及其与裂缝的关系，讨论了不同裂缝宽度下环境因素的影响以及钢筋腐蚀速度．
Experiment studies show that steel corrosion is not caused by cracks of concrete structure in all cases as known.The relationship among steel corrosion and cracks,the influence of environments on steel corrosion with various crack widths,and the velocity of corrosion are discussed in this article.