Thermal Stability of Fe_2O_3 Nanowires

Thermal Stability of Fe_2O_3 Nanowires
下载PDF
导出
摘要 The thermal stability of α-Fe203 and γ-Fe2O3 nanowires was studied by post annealing the samples at different temperatures. Before and after annealing, the samples were characterized by X-ray diffraction and scanning electron microscopy. The α-Fe2O3 nanowires are stable at the temperatures up to 600℃, and the crystalline structure becomes more perfect after annealing. This behavior supplies a way to improve the quality of the α-Fe2O3 nanowires. The γ-Fe2O3 nanowires become unstable when annealed at 350℃. Raman spectra of both nanowires have been measured, which also indicate that the γ-Fe203 nanowires are transformed into α-Fe2O3 under the strong laser beam. The thermal stability of α-Fe203 and γ-Fe2O3 nanowires was studied by post annealing the samples at different temperatures. Before and after annealing, the samples were characterized by X-ray diffraction and scanning electron microscopy. The α-Fe2O3 nanowires are stable at the temperatures up to 600℃, and the crystalline structure becomes more perfect after annealing. This behavior supplies a way to improve the quality of the α-Fe2O3 nanowires. The γ-Fe2O3 nanowires become unstable when annealed at 350℃. Raman spectra of both nanowires have been measured, which also indicate that the γ-Fe203 nanowires are transformed into α-Fe2O3 under the strong laser beam.
出处 《Journal of Materials Science & Technology》 SCIE EI CAS CSCD 2008年第4期594-596,共3页 材料科学技术(英文版)
基金 the National Natural Science Foundation of China under grant Nos.10374003 and 10434010.
关键词 Fe2O3 nanowire Thermal stability Structural transformation Fe2O3 nanowire Thermal stability Structural transformation
  • 相关文献

参考文献21

  • 1[1]T.Grygar,P.Bezdicka,A.Domenech-Carbo,F.Marken,L.Pikna and G.Cepria:Analyst,2002,127(8),1100.
  • 2[2]N.Mimura,I.Takahara,M.Saito,T.Hattori,K.Ohkuma and M.Ando:Catal.Today,1998,45,61.
  • 3[3]A.P.Caricato,Y.V.Kudryavtsev,G.Leggieri,A.Luches,and S.A.Mulenko:J.Phys.D-Appl.Phys.,2007,40(16),4866.
  • 4[4]K.Hayashi,K.Iwasaki,H.Morii,B.Xia,and K.Okuyama:J.Nanopart.Res.,2001,3(2-3),149.
  • 5[5]C.V.Gopal Reddy,K.kalyana Seela and S.V.Manorama:Int.J.Inorg.Mater.,2000,2(4),301.
  • 6[6]Y.Y.Fu,J.Chen and H.Zhang:Chem.Phy.Lett.,2001,350,491.
  • 7[7]Y.Y.Fu,R.M.Wang,J.Xu,J.Chen,Y.Yan,A.V.Narlikar and H.Zhang:Chem.Phys.lett.,2003,379,373.
  • 8[8]Y.Y.Xu,X.F.Rui,Y.Y.Fu and H.Zhang:Chem.Phys.Lett.,2005,410,36.
  • 9[9]X.G.Wen,S.H.Wang,Y.Ding,Z.L.Wang and S.H.Yang:J.Phys.Chem.B.,2005,109(1),215.
  • 10[10]Y.L.Chueh,M.W.Lai,J.Q.Liang,L.J.Chou and Z.L.Wang:Adv.Funct.Mater.,2006,16(17),2243.

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部