摘要
The influences of plastic deformation, aging treatment, and alloying elements on the texture of Cu-Cr-Zr alloys were ex- plored. The texture component and intensity of Cu-Cr-Zr alloys under various working conditions after aging treatment were characterized using the orientation distributing function （ODF）. The influence of Zr content on the texture of Cu-Cr-Zr alloys was also analyzed. The reduction pass and deformation level were primary factors influencing the texture. Rolling texture appeared in a rolled plate and the fibrous textures of {111} and {001} were detected after 80% deformation. Fibrous texture with a main constituent of {111} improved the tensile strength of the alloy wire. The texture contents of {110}〈331〉 and {110}〈112〉 were predominated, whereas, those of {113}〈332〉 and {112}〈111〉 were in the minority in the Cu-Cr-Zr alloy with a higher Zr content （〉0.5wt%）. However, in the samples with a lower Zr content （〈0.1wt%）, the texture contents of {113}〈332〉, {112}〈111〉, and {111}〈110〉 were in the majority.
The influences of plastic deformation, aging treatment, and alloying elements on the texture of Cu-Cr-Zr alloys were ex- plored. The texture component and intensity of Cu-Cr-Zr alloys under various working conditions after aging treatment were characterized using the orientation distributing function （ODF）. The influence of Zr content on the texture of Cu-Cr-Zr alloys was also analyzed. The reduction pass and deformation level were primary factors influencing the texture. Rolling texture appeared in a rolled plate and the fibrous textures of {111} and {001} were detected after 80% deformation. Fibrous texture with a main constituent of {111} improved the tensile strength of the alloy wire. The texture contents of {110}〈331〉 and {110}〈112〉 were predominated, whereas, those of {113}〈332〉 and {112}〈111〉 were in the minority in the Cu-Cr-Zr alloy with a higher Zr content （〉0.5wt%）. However, in the samples with a lower Zr content （〈0.1wt%）, the texture contents of {113}〈332〉, {112}〈111〉, and {111}〈110〉 were in the majority.