摘要
The conversion coating was formed by dipping AA6061 in a fluorotitanate/zirconate acid and amino trimethylene phosphonic acid （ATMP） solution at room temperature. The formation process and the anti-corrosion performance of the conversion coating were investigated using electrochemical test and salt spray test （SST）, respectively. The electrochemical test shows that the Zr/Ti and ATMP coating improves the corrosion resistance of AA6061 as good as the chromate （VI） coating. But the results of SST show that the corrosion resistance of Zr/Ti and ATMP coating is not as good as the chromate （VI） coating. The corrosion area is less than 2% after 72 h.
The conversion coating was formed by dipping AA6061 in a fluorotitanate/zirconate acid and amino trimethylene phosphonic acid （ATMP） solution at room temperature. The formation process and the anti-corrosion performance of the conversion coating were investigated using electrochemical test and salt spray test （SST）, respectively. The electrochemical test shows that the Zr/Ti and ATMP coating improves the corrosion resistance of AA6061 as good as the chromate （VI） coating. But the results of SST show that the corrosion resistance of Zr/Ti and ATMP coating is not as good as the chromate （VI） coating. The corrosion area is less than 2% after 72 h.
基金
supported by the Science and Technology Plan Project of Liaoning Province,China(No.2006221011).