摘要
考察了Ti-43Al-9V钛铝金属间化合物的受阻收缩,评价了Ti-43Al-9V在离心浇注条件下的气孔缺陷。Ti-43Al-9V的受阻收缩率较大。在离心浇注条件下,Ti-43Al-9V棒形件出现了以卷入性气孔为主,同时伴有反应气孔的气孔缺陷。
In this paper, the degree to Ti -43Al -9V casting shrinks have been measured. Casting defects of Ti -43Al -9V used the centrifugal casting is also researched. Ti -43Al -9V has great casting shrinks in the process of cooling but the ability of compensating shrinks is bad. The immixture air hole is the main air defects of casting.
出处
《大庆师范学院学报》
2008年第5期98-100,共3页
Journal of Daqing Normal University
关键词
受阻收缩率
卷入性气孔
反应性气孔
casting shrinks
involvement of air hole
reaction of air hole