Ridge InGaN multi-quantum-well-structure （MQW） edge-emitting laser diodes （LDs） were grown on （0001） sapphire substrates by low-pressure metal-organic chemical vapour deposition （MOCVD）. The dielectric TiO2/SiO2 front and back facet coatings as cavity mirror facets of the LDs have been deposited with electron-beam evaporation method. The reflectivity of the designed front coating is about 50% and that of the back high reflective coating is as high as 99.9%. Under pulsed current injection at room temperature, the influences of the dielectric facets were discussed. The threshold current of the ridge GaN-based LDs was decreased after the deposition of the back high reflective dielectric mirrors and decreased again after the front facets were deposited. Above the threshold, the slope efficiency of the LDs with both reflective facets was larger than those with only back facets and without any reflective facets. It is important to design the reflectivity of the front facets for improving the performance of GaN-based LDs.
Ridge InGaN multi-quantum-well-structure （MQW） edge-emitting laser diodes （LDs） were grown on （0001） sapphire substrates by low-pressure metal-organic chemical vapour deposition （MOCVD）. The dielectric TiO2/SiO2 front and back facet coatings as cavity mirror facets of the LDs have been deposited with electron-beam evaporation method. The reflectivity of the designed front coating is about 50% and that of the back high reflective coating is as high as 99.9%. Under pulsed current injection at room temperature, the influences of the dielectric facets were discussed. The threshold current of the ridge GaN-based LDs was decreased after the deposition of the back high reflective dielectric mirrors and decreased again after the front facets were deposited. Above the threshold, the slope efficiency of the LDs with both reflective facets was larger than those with only back facets and without any reflective facets. It is important to design the reflectivity of the front facets for improving the performance of GaN-based LDs.
基金
supported by the National High Technology Program of China (Grant No 2007AA03Z403)
the National Natural Science Foundation of China (Grant Nos 60776042 and 60477011)
National Basic Research Program of China (Grand No2006CB921607)