摘要
Superfine graphite powder was prepared by ball-milling exfoliated graphite containing anhydrous CuCl2 in planetary ball milling systems. Nano-scale CuCl2 graphite intercalation compounds were synthesized by heating a mixture of anhydrous CuCl2 and graphite nanosheets. Scanning electron microscopy, energy-dispersive X-ray spectroscopy and high-resolution transmission electron microscopy were performed to characterize the microstructures of stage-1 nano-scale CuCl2 graphite intercalation compounds. The structure and components of the domain wall and core in the nano-scale CuCl2 graphite intercalation compounds are described. The results show that the content of CuCl2 in the mixture plays a crucial role in the size of the nano-scale CuCl2 graphite intercalation compound.
Superfine graphite powder was prepared by ball-milling exfoliated graphite containing anhydrous CuCl2 in planetary ball milling systems. Nano-scale CuCl2 graphite intercalation compounds were synthesized by heating a mixture of anhydrous CuCl2 and graphite nanosheets. Scanning electron microscopy, energy-dispersive X-ray spectroscopy and high-resolution transmission electron microscopy were performed to characterize the microstructures of stage-1 nano-scale CuCl2 graphite intercalation compounds. The structure and components of the domain wall and core in the nano-scale CuCl2 graphite intercalation compounds are described. The results show that the content of CuCl2 in the mixture plays a crucial role in the size of the nano-scale CuCl2 graphite intercalation compound.
基金
the National Natural Science Fund(50774071) ;the Natural Science Foundation of Hubei Province(2004ABA090).