摘要
The compound nano-ZnO modified with Ce was prepared by homogeneous precipitation.IR,XRD and dynamic experiments show that the crystal size of nano-ZnO desulfurizer is decreased after being modified with Ce and its desulfurization activities are improved greatly.When calcined at 270 ℃,Ce distributes evenly on the ZnO particle surface as amorphous state oxides,and the amorphous ZnO·H2O also exists;when the calcining temperature is 570 ℃,the crystal CeO2 separates out and the amorphous structure of zinc oxide disappears,at the same time,the crystal is perfect and its size increases,but the desulfurization activities decrease.The desulfurization product of nano-ZnO modified with Ce was analyzed with XPS.The results show that the adsorption compound of HS,S and ZnS exists on the surface of the desulfurizer.
The compound nano-ZnO modified with Ce was prepared by homogeneous precipitation. IR, XRD and dynamic experiments show that the crystal size of nano-ZnO desulfurizer is decreased after being modified with Ce and its desulfurization activities are improved greatly. When calcined at 270 ℃, Ce distributes evenly on the ZnO particle surface as amorphous state oxides, and the amorphous ZnO · H2O also exists; when the calcining temperature is 570 ℃, the crystal CeO2 separates out and the amorphous structure of zinc oxide disappears, at the same time, the crystal is perfect and its size increases, but the desulfurization activities decrease. The desulfurization product of nano-ZnO modified with Ce was analyzed with XPS. The results show that the adsorption compound of HS, S and ZnS exists on the surface of the desulfurizer.
基金
the National Natural Science Foundation of China(Grant No.50478026)
the Science Foundation for Young Scientists of Harbin University of Science and Technology(Grant No.2008XQJZ039)