通过对相对切口深度为0.2、0.3、0.40、.5的钢纤维高强混凝土三点弯曲试验,研究钢纤维体积率对高强混凝土断裂性能的影响。结果表明:在相对切口深度为0.20、.3、0.4、0.5的条件下,随着钢纤维体积率的增大,钢纤维高强混凝土断裂韧度和断裂能均显著增加。通过对试验结果的统计分析,分别建立断裂韧度、断裂能与劈拉强度之间的关系式。
Through the three-point bending test on notched beams of steel fiber reinforced high-strength concrete(SFHSC) with the relative notch depth of 0. 2,0.3,0.4 and 0.5, the effect of the steel fiber volume fraction upon fracture properties of high strength concrete was studied. The results show that under the four relative depth conditions the SFRC fracture toughness and fracture energy significantly increase as the steel fiber volume fraction increases. Based on the statistical analysis of test results, the formula were established for the relationship of the fracture toughness and fracture energy with the tensile strength of steel fiber reinforced high strength concrete respectively.
出处
《工业建筑》
CSCD
北大核心
2008年第8期50-53,108,共5页
Industrial Construction
关键词
钢纤维体积率
高强混凝土
三点弯曲试件
断裂韧度
断裂能
steel fiber volume fraction high strength concrete three-point bending test beam fracture toughness fracture energy