摘要
通过球团试验,得出用大冶铁精矿生产高质量球团矿的措施。试验结果表明:在大冶铁精矿-0.074mm粒级含量为93.35%、粘结剂临安膨润土用量为2%、水分为8.0%条件下,通过严格控制造球时间、给料与给水速度和给料与给水方式等,可获得优质球团矿,其生球0.5 m落下强度>3.8次,抗压强度12.0 N个/,爆裂温度>450℃,成品球抗压强度>2.5 kN/个。
The measures for producing high quality pellets from Daye iron concentrate are found through pelletizing test. The test result indicates that when using a Daye iron concentrate which contains 93.35 % -0.074 mm fraction, 2% Linan betonite as binder and 8.0% moisture, through strict control of the pelletizing time and the material and water feeding rate and mode, fine quality pellets can be produced. The green balls have a drop strength at 0.5 m greater than 3.8 times, a compressive strength of 12.0 N per ball and a burst temperature of higher than 450 ℃. The compressive strength of the pellet product is greater than 2.5 kN per pellet.
出处
《金属矿山》
CAS
北大核心
2008年第10期67-69,75,共4页
Metal Mine