The amino-tri-（methylenephosphonic acid） layers were adsorbed on the surface of AA6061 aluminum alloy for improving the lacquer adhesion and corrosion inhibition as a substitute for chromate coatings. The surface structure and characteristic of the amino-tri-（methylenephosphonic acid） layers on AA6061 aluminum alloy were investigated by means of XPS and ATR-FTIR analysis. The analyzed results showed that the amino-tri-（methylenephosphonic acid） adsorption layers adsorb on the surface of aluminium alloy via acid-base interaction in a bi-dentate conformation. After the amino-tri-（methylenephosphonic acid） layers were coated with epoxy resin, the layers showed good adhesive strength and favorable corrosion resistance in contrast to chromate coatings.
The amino-tri-（methylenephosphonic acid） layers were adsorbed on the surface of AA6061 aluminum alloy for improving the lacquer adhesion and corrosion inhibition as a substitute for chromate coatings. The surface structure and characteristic of the amino-tri-（methylenephosphonic acid） layers on AA6061 aluminum alloy were investigated by means of XPS and ATR-FTIR analysis. The analyzed results showed that the amino-tri-（methylenephosphonic acid） adsorption layers adsorb on the surface of aluminium alloy via acid-base interaction in a bi-dentate conformation. After the amino-tri-（methylenephosphonic acid） layers were coated with epoxy resin, the layers showed good adhesive strength and favorable corrosion resistance in contrast to chromate coatings.
基金
the Science and Technology Plan Project of LiaoningProvince, China (No.2006221011)