摘要
对热轧板孔洞缺陷的机理及昆钢St12热轧板大气泡孔洞缺陷的成因进行了研究分析,提出了相应的控制措施,取得了较好的效果。
The cavity defects mechanism of hot rolled plates and the cause of big bubbles cavity defects of hot rolled plates of KISC were analyzed. Some relevant prevention and control measures were put forward.
出处
《连铸》
2008年第5期42-44,共3页
Continuous Casting
关键词
热轧板
孔洞缺陷
预防控制
hot rolled plates, cavity defects, prevention and control