摘要
A hypothesis is brought forward that the materials with low propagation loss in both optical and microwave band may exhibit good performance in terahertz （THz） band because THz wave band interspaces those two wave bands. For the purpose-of exploring a kind of low-loss material for THz waveguide, Lu2.1Bi0.9Fe5O12（LuBiIG） garnet films are prepared by liquid phase epitaxy （LPE） method on a gadolinium gallium garnet （GGG） substrate from lead-free flux because of the good properties in both optical and microwave bands. In microwave band, the ferromagnetic resonance （FMR） linewidth of the film 2△H = 2.8-5.1Oe; in optical band, the optical absorption coefficient is 600cm^-1 at visible range and about 100-170cm^-1 when the wavelength is longer than 800nm. In THz range, our hypothesis is well confirmed by a THz-TDS measurement which shows that the absorbance of the film for THz wave is 0.05-0.3 cm 1 and the minimum value appears at 2.3 THz. This artificial ferromagnetic material holds a great promise for magnetic field tunable THz devices such as waveguide, modulator or switch.
A hypothesis is brought forward that the materials with low propagation loss in both optical and microwave band may exhibit good performance in terahertz （THz） band because THz wave band interspaces those two wave bands. For the purpose-of exploring a kind of low-loss material for THz waveguide, Lu2.1Bi0.9Fe5O12（LuBiIG） garnet films are prepared by liquid phase epitaxy （LPE） method on a gadolinium gallium garnet （GGG） substrate from lead-free flux because of the good properties in both optical and microwave bands. In microwave band, the ferromagnetic resonance （FMR） linewidth of the film 2△H = 2.8-5.1Oe; in optical band, the optical absorption coefficient is 600cm^-1 at visible range and about 100-170cm^-1 when the wavelength is longer than 800nm. In THz range, our hypothesis is well confirmed by a THz-TDS measurement which shows that the absorbance of the film for THz wave is 0.05-0.3 cm 1 and the minimum value appears at 2.3 THz. This artificial ferromagnetic material holds a great promise for magnetic field tunable THz devices such as waveguide, modulator or switch.
基金
Supported by the National Basic Research Programme of China under Grant No 2007CB31407, the National Natural Science Foundation of China under Grant No 60721001, and the International S＆T Cooperation Programme of China under Grant No 2006DFA53410.