化学镀Ni-Co-P工艺与性能研究 被引量:6

Study on the Process and Properties of Electroless Ni-Co-P
下载PDF
导出
摘要 采用复合络合剂.柠檬酸钠和乳酸,通过正交试验优化了化学镀Ni—Co-P工艺,并对镀层的形貌、成分、组织结构及性能进行了检测和分析。结果表明,优化后的化学镀Ni-Co-P镀液稳定性好,镀速高;所得镀层为纳米晶结构,晶粒尺寸在40~60nm,具有Ni(Co)(111)取向,整个热处理过程中晶粒没有明显长大,在428℃左右镀层发生重结晶,析出Ni3P相;镀层硬度HV10为8867MPa,在400℃处理后HV10可提高至9892MPa:镀层矫顽力Hc为556.27×79.6A/m,饱和磁化强度坛为48.73(A·m^2)/kg,整个热处理过程中,镀层磁性参数变化不大。镀层具有良好的热稳定性。 In this paper, the electroless Ni-Co-P plating solution was stabilized using two eomplexing agents, sodium citrate, and lactic acid. Furthermore, bath and operation parameters were optimized by orthogonal experiment. Then, the morphology, composition, microstructures and properties of the coatings were detected and analyzed. It was found that the optimized plating solution was stable and of high plating rate. The as-plated Ni-Co-P films had a grain size of 40-60 nm and strong Ni(Co) (111) orientation. During heat treatment, the grain didn't grow obviously, recrystallization occurred at 428 ℃, in which Ni3P separated out. The hardness HV10 of the as-plated coatings was 8867 MPa and increased to the maximum 9892 MPa after heated at 400 ℃ for 1 h. The coercivity (H0 was 556.27×79.6 A/m and saturation magnetization (Ms) was 48.73 (A·m^2)/kg. The values of the Hc and Ms didn't change obviously during heat treatment. The Ni-Co-P film show excellent thermal stability.
机构地区 太原理工大学
出处 《稀有金属材料与工程》 SCIE EI CAS CSCD 北大核心 2008年第11期1982-1986,共5页 Rare Metal Materials and Engineering
基金 国家自然科学基金(50471070 50644041) 山西省自然科学基金(20051050) 教育部新世纪优秀人才支持计划(NCET-04-0257)
关键词 化学镀 Ni-Co-P合金 组织结构 性能 electroless Ni-Co-P alloy microstructure property
  • 相关文献

参考文献13

  • 1Li Ning(李宁).Application Technology Electroless Plating(化学镀应用技术)[M].Beijing: Chemistry Industry Press, 2003:362
  • 2Bi X F et al. Mater Sci Eng [J], 2003, 344:74
  • 3Park D Yet al. Electrochim Acta[J], 2002, 47:2893
  • 4Murthy S K et al. JElectrochem Soc[J], 2004, 151(1): C1
  • 5Homma T et al. J Electrochem Soc[J], 2000, 147(11): 4138
  • 6Fenineche N et al. Surf Coat Technol[J], 1997, 88:264
  • 7Younan M Met al. J Appl Electrochem[J], 2002, 32:439
  • 8宣天鹏,郑晓华,刘玉,邓宗钢.镍钴离子浓度比对化学镀Co-Ni-P合金组织结构和性能的影响[J].稀有金属,1998,22(2):111-115. 被引量:12
  • 9Lee D N, Hur K H. Scripta Mater[J], 1999, 40(12): 1333
  • 10杨海燕,卫英慧,毕虎才,侯利锋,郭耀文,余春燕,许并社.压铸镁合金AZ91D手机内构件的Ni-P化学镀[J].稀有金属材料与工程,2005,34(12):1978-1981. 被引量:4

二级参考文献14

共引文献14

同被引文献67

引证文献6

二级引证文献21

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部