Four kinds of Mg alloys reinforced with carbon fibres were fabricated by a gas pressure infiltration technique. The fibres were pre-coated a SiO2 layer prior to fabrication. DifFerent microstructures and interactions in the fibre-matrix interface of these composites were observed by transmission electron microscopy （TEM）. The results showed that the interracial interaction strongly depended on the content of Al in the Mg-based matrices. The microstructure of the interface could then be controlled by adjusting the Al content of the Mgbased matrix. In addition, fibres extracted from different Mg-based matrix all had some degradation owing to the interracial reaction and the fibre-matrix interdiffusion.
Four kinds of Mg alloys reinforced with carbon fibres were fabricated by a gas pressure infiltration technique. The fibres were pre-coated a SiO2 layer prior to fabrication. DifFerent microstructures and interactions in the fibre-matrix interface of these composites were observed by transmission electron microscopy （TEM）. The results showed that the interracial interaction strongly depended on the content of Al in the Mg-based matrices. The microstructure of the interface could then be controlled by adjusting the Al content of the Mgbased matrix. In addition, fibres extracted from different Mg-based matrix all had some degradation owing to the interracial reaction and the fibre-matrix interdiffusion.