二氧化硅对纳米氧化锌热稳定性的影响 被引量:1

Effect of silica on thermal stability of nano-sized zinc oxide
下载PDF
导出
摘要 为了抑制纳米氧化锌的光催化活性,通过硅酸钠水解生成二氧化硅对氧化锌进行表面包覆。对包覆二氧化硅的纳米氧化锌进行热处理,研究了二氧化硅对纳米氧化锌热稳定性的影响。利用X射线衍射仪(XRD)、氮吸附仪和高分辨透射电子显微镜(HRTEM)对所得样品进行表征,并对纳米氧化锌的光稳定性进行评价。结果表明,合适的热处理温度为600℃,适当的热处理有助于提高包覆层的均匀性和致密性,而且在热处理过程中纳米氧化锌的晶粒生长得到了有效抑制。 Nano - sized zinc oxide was coated with silica by using sodium silicate as raw material to inhibit its photocatalytic activity. SiO2 - coated zinc oxide was heat - treated, and the effect of silica on thermal stability of nano - sized zinc oxide was investigated. The prepared samples were characterized by XRD, BET, and HRTEM. The photo - stability of nano - sized zinc oxide was also evaluated. Results showed that the suitable calcination tempreture was 600 ℃, and the homogeneity and densification of coating layer was improved from suitable heat treatment. Moreover, the growth of nano- sized zinc oxide grains was efflectively suppressed in the process of heat treatment. Key words : silica ; nano - sized zinc oxide ; surface treatment ; thermal stability
机构地区 江苏工业学院
出处 《无机盐工业》 CAS 北大核心 2008年第12期21-23,共3页 Inorganic Chemicals Industry
基金 江苏省富民强县项目(BE2006373) 常州青年科技人才资助项目(CQ2006009)
关键词 二氧化硅 纳米氧化锌 表面处理 热稳定性 silica nano - sized zinc oxide surface treatment thermal stability
  • 相关文献

参考文献6

二级参考文献34

  • 1Laubil M W Bruttel P A.Determination of the Oxidative Stability of Fats and Oils [J].Journal of the American Oil Chemists′Society,1986,63(6):792-795.
  • 2[1]Misono M, Nojiri N. Appl Catal, 1990, 64(1/2): 1
  • 3[2]Schindler G-P, Ui T, Nagai K. Appl Catal A, 2001, 206(2): 183
  • 4[3]Cavani F, Mezzogori R, Pigamo A, Trifiro F, Etienne E. Catal Today, 2001, 71(1/2): 97
  • 5[6]Sun L, Bolton J R. J Phys Chem, 1996, 100(10): 4127
  • 6[7]Seiferth O, Wolter K, Dillmann B, Klivenyi G, Freund H-J, Scarano D, Zecchina A. Surf Sci, 1999, 421(1/2): 176
  • 7Choi W, Terrain A, Hoffmann M R. The Role of Metal Ion Dopants in Quantum-sized TiO2: Correlation Between Photoreactivity and Charge Carrier Recombination Dynamics [J]. J. Phys. Chem., 19 94, 98(51): 13669-13679.
  • 8Laubil M W, Bruttel P A. Determination of the Oxidative Stability of Fats and Oils [J]. Journal of the American Oil Chemists'Society, 1986, 63(6): 792-795.
  • 9Frank J, Ceil J V, Freaso R. Automatic Determination of Oxidation Stability of Oil and Fatty Products [J]. Food Technology,1982, (6): 71-76.
  • 10Masui T, Yamamoto M, Sakuta T. Synthesis of BN-coated CeO2 Fine Powder as a New UV Blocking Material [J]. J. Mater.Chem., 2000, 10(2): 353-357.

共引文献71

同被引文献10

  • 1Lm DM. Key Engineering Material s [J],1996,115 : 209 - 232.
  • 2Hench Larry L. J Am Ceram Soc[J] , 1998, 81 (7) :1705 - 1728.
  • 3Choi SH,Kim EG,Park JN, et al. Large -scale synthesis of hexagonalpyramid - shaped ZnO nanocrystals from thermolysis of Zn - oleatecomplex [J]. J Phys Chem B, 2005 ,109(31):14792-14794.
  • 4Suge T, Ishikawa K,Kawasaki A, et al. Evaluation of postt -treatmentsolutions for clinical use with the calcium pHos-pHate precipitationmethod [J]. Hourna Dent,1999,27(7):487 -496.
  • 5Hench. Bioceramics [J]. Am. Ceram, Soc, 1998, 81 (7): 1705-1728.
  • 6Ducheyne P,Beight J,GucklerJ,et al. Apreliminary study on osteoinduction of two kinds of calcium phosphate ceramics [J]. Biomaterials, 1990,20 ! 1799.
  • 7Luo L X, Feng CG. linchan Huaxue Yu Gongye/Chemistryand Industry of Forest Products,2004,24: 83 - 86.
  • 8牛丽娜,陈吉华,方明,杨聚才,肖玉鸿,倪峰.不同形貌氧化锌对复合树脂抗变异链球菌活性的影响[J].华西口腔医学杂志,2009,27(2):210-212. 被引量:8
  • 9杨立斗,孙帆,王刚,袁艳波,苏军,张文云,黄明华.羟基磷灰石晶须/纳米氧化锌复合抗菌人工骨体外极限降解实验[J].昆明医科大学学报,2014,35(5):24-28. 被引量:2
  • 10刘静,母瑞虹,黄洁.含碳酸盐氟羟磷灰石新型抛光膏的应用观察[J].北京口腔医学,2002,10(2):82-84. 被引量:4

引证文献1

二级引证文献3

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部