道次间隔时间对Ti-1Al-1Fe合金热压缩变形组织和性能的影响 被引量:1

Effects of Interval Time on Structure and Properties of Ti-1Al-1Fe Titanium Alloy During Two-stage Hot Compression Deformation
下载PDF
导出
摘要 在Gleebe-1500热力模拟机上,采用两道次间隙式等温热压缩实验,研究了Ti-1Al-1Fe钛合金道次间隔时间对合金组织和性能的影响。结果表明:在热压缩变形道次间保温停歇之后,流变应力明显降低,保温停歇时间越长,合金软化率减小;变形及停歇保持温度越高,合金软化程度越高。 The effects of interval time on structure and properties of Ti-1Al-1Fe alloy during two-stage hot compression deformations were investigated by isothermal interrupted hot compression on Gleeble-1500 thermal-mechanical simulator. The results show that flow stress drops obviously after interval. The softening fraction reduces as the time of the isothermal gap prolongs; and the higher the temperature of deformation and interval, the higher the softening fraction.
作者 李梁 蒋鹏
出处 《热加工工艺》 CSCD 北大核心 2008年第24期49-51,共3页 Hot Working Technology
关键词 Ti-1Al-1Fe合金 两道次热压缩变形 软化率 间隔时间 Ti-1Al-1Fe alloy two-stage hot compression deformation softening fraction interval time
  • 相关文献

参考文献5

二级参考文献30

  • 1张辉,彭大暑,杨立斌,孟力平.Recrystallization model for hot-rolling of 5182 aluminum alloy[J].中国有色金属学会会刊:英文版,2001,11(3):382-386. 被引量:3
  • 2ZHANG Hui,PENG Da shu,YANG Li bin,MENG Li ping (Department of Materials Science and Engineering, Central South University, Changsha 410083, China).Flow stress equation for multipass hot-rolling of aluminum alloys[J].Journal of Central South University of Technology,2001,8(1):13-17. 被引量:7
  • 3毛新平.薄板坯连铸连轧铁素体轧制工艺[J].钢铁,2004,39(5):71-74. 被引量:28
  • 4ZHOU M, CLODE M P. Constitutive Equations for Modeling Flow Softening Due to Dynamic Recovery and Heat Generation During Plastic Deformation [J]. Mechanics of Materials, 1998,27(2): 63-76.
  • 5CHO S H, KIM S I, YOO Y C. Determination of No-recrystallization Temperature of Invar Alloy by Fractional Softening Measurement During the Multistage Deformation [J]. Journal of Materials Science Letters, 1997,16(22): 1836-1837.
  • 6SONNINO C, FORD T, VANARK V. Potentiometric and Potentiostatic Determination of the Corrosion Rate of Welded 2519 Aluminum Alloy [J]. ASTM Special Technical Publication, 1991, (1134): 132-140.
  • 7DEVICENT S M, DEVLETIAN J H, GEDON S A. Weld Properties of the Newly Developed 2519-T87 Aluminum Armor Alloy [J]. Welding Journal, 1988,67(7): 33- 43.
  • 8DYMEK S, DOLLAR M. TEM Investigation of Age-hardenable Al 2519 Alloy Subjected to Stress Corrosion Cracking Tests[J]. Materials Chemistry and Physics, 2003,82(1):1-3.
  • 9CHIA E H, MCQUEEN H J. Microstructure Control in Aluminum Alloy: Deformation, Recovery and Recrystallization[M].NewYork:TMS, 1985.
  • 10KWON O, DEARDO A J. On the Recovery and Recrystallization Which Attend Static Softening in Hot-deformed Copper and Aluminum[J]. Acta Metallurgical, 1990,38(1): 41-54.

共引文献18

同被引文献8

引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部