摘要
Particular properties of Ti2O and TiNx prepared by thermal decomposition were introduced. A precursor prepared by titanium powder reacting with oxalate acid was thermally decomposed in nitrogen atmosphere at 840℃ for 15 min, and relatively pure Ti2O was then obtained. Conductive TiNx was also prepared after altering reaction conditions. Samples were characterized by resistivity, X-ray powder diffraction, transmission electron microscope, Ultraviolet-Visible diffuse reflection, and electromagnetic shielding efficiency. The results indicate that both Ti2O and TiNx have good conductivity. Moreover, Ti2O shows a better solar photocatalytic activity and TiNx does well in the electromagnetic shield.
Particular properties of Ti2O and TiNx prepared by thermal decomposition were introduced. A precursor prepared by titanium powder reacting with oxalate acid was thermally decomposed in nitrogen atmosphere at 840℃ for 15 min, and relatively pure Ti2O was then obtained. Conductive TiNx was also prepared after altering reaction conditions. Samples were characterized by resistivity, X-ray powder diffraction, transmission electron microscope, Ultraviolet-Visible diffuse reflection, and electromagnetic shielding efficiency. The results indicate that both Ti2O and TiNx have good conductivity. Moreover, Ti2O shows a better solar photocatalytic activity and TiNx does well in the electromagnetic shield.
基金
financially supported by the Science Fund from Tongji University (No. 1380219042)