Acetalizatioin on the blend fibers of poly(vinyl alcohol) (PVA) and soybean protein (SP) was studied by using dialdehydes as cross-linking agents. The optimal acetalization conditions were determined by Latin square experiment, where the modified fibers with good mechanical properties can be achieved by treating in 41 g/L dialdehyde solution at 67 ℃ for 9 min. The cross-linking reactions of PVA and SP with dialdehydes were confirmed by Fourier transform infrared (FTIR) spectroscopy. Tensile test and boiling water shrinkage measurements showed that the physical properties of PVA/SP fibers crosslinked by dialdehydes were improved comparing with those formalized fibers.
Acetalizatioin on the blend fibers of poly （vinyl alcohol） （PVA） and soybean protein （SP） was studied by using dialdehydes as cross-linking agents. The optimal acetalization conditions were determined by Latin square experiment, where the modified fibers with good mechanical properties can be achieved by treating in 41 g/L dialdehyde solution at 67 ℃ for 9 min. The cross-linking reactions of PVA and SP with dialdehydes were confirmed by Fourier transform infrared （FTIR） spectroscopy. Tensile test and boiling water shrinkage measurements showed that the physical properties of PVA/SP fibers crosslinked by dialdehydes were improved comparing with those formalized fibers.